MEMS Device and Fabrication Method

ABSTRACT

A method and structure for uncovering captive devices in a bonded wafer assembly comprising a top wafer and a bottom wafer. One embodiment method includes forming a plurality of cuts in the top wafer and removing a segment of the top wafer defined by the plurality of cuts. The bottom wafer remains unsingulated after the removal of the segment.

CROSS-REFERENCE TO RELATED APPLICATIONS

This application is related to co-filed and commonly owned U.S. Patent Application Ser. No. [Attorney Docket No. TI-65482], “Bonded Wafer Assembly System and Method,” which application is hereby incorporated herein by reference.

TECHNICAL FIELD

Embodiments of the present invention relate to a MEMS device and fabrication method, and more particularly to a device and method for uncovering captive structures on a MEMS bonded wafer assembly.

BACKGROUND

In the production of semiconductors, and particularly in the production of microelectromechanical system (MEMS) devices, chips are produced in an array often times having as many 30 or more devices on a single wafer. Typically, these devices are formed on a first wafer, and then a second wafer is bonded to the first wafer. Cavities may be formed between the wafers in various areas, for example above the MEMS components or above the bond pads. After the wafers are bonded together, the bond pads, or other structures to which access is desired for further testing and processing, are completely covered by the top wafer. These structures generally need to be exposed prior to testing and processing of the embedded devices.

Previously, singulation of these devices was performed to separate the devices from each other and expose the bond pads prior to the testing and processing of the devices. In previous methods, the wafer assembly would be completely singulated into individual devices, and the individual devices would be arranged and held in place on a tape for testing and processing. The devices may be singulated either before or after being placed on the tape.

The use of a tape in such a process may give rise to various problems. In particular, the shifting of chips on the tape may cause alignment problems with a testing probe or other equipment. Such problems tend to increase test time due to extensive wafer alignment measurements, and also tend to increase the down time during testing resulting from misalignment. Both of these factors may contribute to increased cost of semiconductor production.

SUMMARY OF THE INVENTION

These and other problems are generally solved or circumvented, and technical advantages are generally achieved, by preferred embodiments of the present invention in which captive structures of MEMS devices in a bonded wafer assembly are uncovered while the MEMS devices remain together, unsingulated, in the wafer assembly.

In accordance with a preferred embodiment, a method for uncovering captive structures in a bonded wafer assembly comprises forming a plurality of microelectromechanical (MEMS) devices and rows of contact zones on a bottom wafer, bonding a top wafer to the bottom wafer, thereby covering the MEMS devices and contact zones, cutting a plurality of linear cuts in the top wafer between adjacent MEMS devices and parallel to the rows of contact zones, and removing a segment of the top wafer defined by the plurality of cuts, wherein the bottom wafer remains unsingulated, wherein at least one of the rows of contact zones is uncovered, and wherein the adjacent MEMS devices remain covered.

In accordance with another preferred embodiment, a MEMS bonded wafer assembly comprises an unsingulated bottom wafer, an array of MEMS devices disposed on the bottom wafer, the array having columns and rows, at least one row of bond pads disposed on the bottom wafer for each of the rows of MEMS devices, a top wafer bonded to the bottom wafer in a perimeter around each of the MEMS devices, and between the MEMS devices and their associated bond pads, wherein the top wafer is partially singulated into rows, each top wafer row covering a respective row of the rows of MEMS devices as well as regions between the MEMS devices in the respective row, and wherein the top wafer does not cover the bond pads.

In accordance with another preferred embodiment, a method of processing a MEMS bonded wafer assembly comprises forming a plurality of parallel partial cut pairs extending only partially through a top wafer, forming a plurality of parallel full cuts extending fully through the top wafer and between respective partial cut pairs, removing segments of the top wafer defined by the partial cut pairs, the segments overlying the captive structures disposed therebeneath on a bottom wafer, and processing at least one of the captive structures while the bottom wafer remains unsingulated.

An advantage of an embodiment is that MEMS devices may be tested and further processed without singulation of the wafer. Another advantage of an embodiment is that the alignment and cost issues of associated with previous methods may be avoided.

BRIEF DESCRIPTION OF THE DRAWINGS

For a more complete understanding of the embodiments, and the advantages thereof, reference is now made to the following descriptions taken in conjunction with the accompanying drawings, in which:

FIG. 1 is a top plan view of a bonded wafer assembly having a plurality of devices disposed thereon;

FIG. 2 is a side elevation view of the bonded wafer assembly of FIG. 1 taken along section line A-A;

FIG. 3A is a side elevation view of the bonded wafer assembly of FIG. 2 at a subsequent step in production;

FIG. 3B is a partial plan view of the bonded wafer assembly of FIG. 3A;

FIG. 4A is a side elevation view of the bonded wafer assembly of FIG. 3A at a subsequent step in production;

FIG. 4B is a partial plan view of the bonded wafer assembly of FIG. 4A;

FIG. 5A is a side elevation view of the bonded wafer assembly of FIG. 4A at a subsequent step in production;

FIG. 5B is a partial plan view of the bonded wafer assembly of FIG. 5A;

FIG. 6A is a side elevation view of the bonded wafer assembly of FIG. 5A at a subsequent step in production;

FIG. 6B is a partial plan view of the bonded wafer assembly of FIG. 6A;

FIG. 7A is a side elevation view of the bonded wafer assembly of FIG. 6A at a subsequent step in production;

FIG. 7B is a partial plan view of the bonded wafer assembly of FIG. 7A;

FIG. 8A is a side elevation view of the bonded wafer assembly of FIG. 7A at a subsequent step in production;

FIG. 8B is a partial plan view of the bonded wafer assembly of FIG. 8A;

FIG. 9 is a side elevation view of a bonded wafer assembly during testing of a captive structure; and

FIG. 10 is a process flow diagram depicting a process for gaining access to captive structures in a bonded wafer assembly.

DETAILED DESCRIPTION OF EXEMPLARY EMBODIMENTS

Various embodiments will now be discussed in detail with reference made to the accompanying figures. It should be appreciated, however, that the present invention provides many applicable inventive concepts that can be embodied in a wide variety of specific contexts. The specific embodiments discussed herein are merely illustrative of specific ways to make and use the invention, and do not limit the scope of the invention.

The present invention will be described with respect to preferred embodiments in a specific context, namely the fabrication of a particular microelectromechanical system (MEMS) device formed on a silicon wafer with a glass cover or cover assembly that includes a glass cover wafer, as used in, for example, a digital micromirror device (DMD). The concepts may also be applied, however, to other MEMS structures and make use of other materials as well. For example, the MEMS devices may be other spatial light modulators, other optical devices such as optical switches, mechanical or electrical switches, mechanical transducers such as pressure sensors, accelerometers, piezoelectrics, gyroscopes, biosensors, chemical sensors, chemical reactors, electrostatic actuators, micro-motors, micro-relays, fluidic devices such as pneumatic valves, membrane pumps, flow sensors, etc.

With respect to DMDs, and as fully explained in commonly owned U.S. Pat. No. 7,378,293 to Diep, “MEMS Fabrication Method,” issued on May 27, 2008, which patent is hereby incorporated herein by reference, DMD MEMS devices may be formed by bonding a glass cover to a semiconductor wafer containing the MEMS components, circuitry, bond pads, etc. Prior art methods for wafer singulation use a partial-saw and break method. That is, a saw cut creates a fault-line so that the dice may be separated using an impact tool. U.S. Pat. No. 7,378,293 also teaches a partial-saw and full-saw method. That is, a first saw cut is made partially into the cover, and a second saw cut is made all the way through the cover and the wafer to separate the dice. In either approach, singulation of the wafer assembly into individual dice is followed by removal of the swizzle sticks (in these examples the portion of the cover that is covering the bond pads) to expose the bond pads. Testing and further processing of the dice then may be performed. Further details for DMD device structures, applications, and processes (e.g., sawing and glass removal) may be referenced in U.S. Pat. No. 7,378,293, and thus are not described herein in detail except to the extent helpful in clarifying the described embodiments.

Referring now to FIG. 1, there is shown a wafer 100 populated with a plurality of devices 102. By way of example, FIG. 1 shows the wafer 100 to be populated with thirty-six devices 102. Alternatively, fewer devices may be used, or a much greater number of devices 102 may be used in other embodiments. As can be seen in FIG. 1, the arrangement of the devices 102 upon the surface of the wafer 100 creates a grid-like pattern having both horizontal rows and vertical columns. Note that only the horizontal rows are shown in the subsequent figures with the vertical columns omitted for clarity. Note also that the terms “horizontal rows” and “vertical columns” are used herein for convenience, but are arbitrarily chosen and distinguishable only relative to one another unless otherwise noted or apparent from the context.

Referring next to FIG. 2, there is shown a bonded wafer assembly 10 that includes a top wafer 12 and a bottom wafer 14. The bonded wafer assembly 10 shown in FIG. 2 and all subsequent process figures represents a section of the wafer 100 taken across the section line A-A shown in FIG. 1. The top wafer 12 and the bottom wafer 14 are joined by way of a series of adhesive pads 16 disposed in an interstitial space 15. In a typical embodiment, the top wafer 12 has a thickness of approximately 1 millimeter and is constructed from an appropriate semiconductor processing material. Such a material could be, for example, glass, silicon, or gallium arsenide. Furthermore, the top wafer 12 may be of unitary construction, or may be an assembly of multiple layers or substrates. The bottom wafer 14 may also be constructed of any appropriate semiconductor material such as, for example, silicon or gallium arsenide. Also disposed in the interstitial space 15 is at least one device 18. By way of example, the device 18 is illustrated in FIG. 1 as being a MEMS type device, and in particular a DMD device. However, the device 18 may be any appropriate integrated circuit device. The device 18 typically includes a set of contact zones 20, e.g., comprising bonding pads, disposed proximate to, and on either side of, the device 18.

Referring next to FIGS. 3A and 3B, a first partial cut 22 a is made in the top wafer 12. By way of example, the first cut 22 a is shown in FIG. 3A as being positioned on the left side of the device 18 a on the outside of the adhesive pads 16. The first cut 22 may be made by any appropriate means such as, for example, a rotating or reciprocating saw. The first cut 22 a generally should be formed in such a way so as to ensure an accurate and consistent depth. The first cut 22 a typically has a width in the range of approximately 50 microns to approximately 100 microns, although other dimensions may be used for this and the other cuts described herein. As illustrated in FIG. 3A, the first cut 22 a does not cut all the way through the top wafer 12. Rather, the first cut 22 a only cuts partially through the top wafer 12 leaving a tab 24 holding the segment 23 in place. The tab 24 typically has a thickness in the range of about 30 microns to about 80 microns, but may be other dimensions depending on the specific application. As shown in FIG. 3B, the first cut 22 a extends down the full length of the bonded wafer assembly 10.

Referring next to FIGS. 4A and 4B, the process continues by making a second partial cut 22 b in the top wafer 12. By way of example, the second cut 22 b is shown in FIG. 4A as being positioned on the right side of the device 18 a, and on the outside of the adhesive pads 16. The second cut 22 b may be made by any appropriate means such as, for example, a rotating or reciprocating saw. The second cut 22 b generally should be formed in such a way so as to ensure an accurate and consistent depth. Similar to the first cut 22 a, the second cut 22 b typically has a width in the range of approximately 50 microns to approximately 100 microns. As illustrated in FIG. 4A, the second cut 22 b also does not cut all the way through the top wafer 12. Rather, the second cut 22 b only cuts partially through the top wafer 12 leaving a tab 24. The tab 24 typically has a thickness in the range of about 30 microns to about 80 microns. As shown in FIG. 4B, the second cut 22 b extends down the full length of the bonded wafer assembly 10.

Referring next to FIGS. 5A and 5B, the process continues by making a third partial cut 22 c and fourth partial 22 d in the top wafer 12. By way of example, the third cut 22 c is shown in FIG. 5A as being positioned on the left side of the device 18 b, and on the outside of the adhesive pads 16. Likewise, the fourth partial cut 22 d is shown by way of example as being located on the right side of device 18 b and on the outside of the adhesive pads 16. The third and fourth cuts 22 c and 22 d may be made by any appropriate means such as, for example, a rotating or reciprocating saw. The third and fourth cut 22 c and 22 d generally should be formed in such a way so as to ensure an accurate depth that is consistent with the first and second cuts 22 a and 22 b. Similar to the first and second cuts 22 a and 22 b, the third and fourth cuts 22 c and 22 d typically have a width in the range of approximately 50 microns to approximately 100 microns. As illustrated in FIG. 5A, the third and fourth cuts 22 c and 22 d also do not cut all the way through the top wafer 12. Rather, the third and fourth cuts 22 c only cut partially through the top wafer 12 leaving a tab 24 holding the segment 23 in place. The tab 24 typically has a thickness in the range of about 30 microns to about 80 microns. As shown in FIG. 5B, the third and fourth cuts 22 c and 22 d extends down the full length of the bonded wafer assembly 10.

By way of example only, FIGS. 3A-5B illustrate four partial cuts 22 a-22 d being made in the top wafer 12. In practice, any number of partial cuts could be performed depending upon on the number of devices, the number of captured structures to be uncovered, the application, etc.

Referring next to FIGS. 6A and 6B, there is shown the bonded wafer assembly 10 in the next phase of manufacturing. As shown in FIG. 6A, a first complete cut 26 a is made in the top wafer 12. The first complete cut 26 a extends entirely through the top wafer 12, but does not reach the bottom wafer 14, leaving the bottom layer 14 intact. Alternatively, for the complete cuts, the bottom wafer may be partially cut into, as long as the bottom wafer is not singulated. By way of example, the first complete cut 26 a is shown in FIG. 6A as being located to the left of the first partial cut 22 a, and on the outside of the contact zone 20. Similar to the partial cuts 22 a-22 d, the first complete cut 26 a may be made by any appropriate means such as, for example, a rotating or reciprocating saw. The first complete cut 26 a generally should be formed in such a way so as to ensure an accurate and consistent depth. Similar to the partial cuts 22 a-22 d, the first complete cut 26 a typically has a width in the range of approximately 50 microns to approximately 100 microns. As shown in FIG. 6B, the first complete cut 26 a extends down the full length of the bonded wafer assembly 10.

Referring next to FIGS. 7A and 7B, the process continues by making a second complete cut 26 b in the top wafer 12. The second complete cut 26 b extends entirely through the top wafer 12, but leaves the bottom layer 14 intact. By way of example, the second complete cut 26 b is shown in FIG. 7A as being located between second and third partial cuts 22 b and 22 c. The second complete cut 26 b is positioned so as to approximately bisect segment 23 into segment halves or swizzle sticks 28. Typically, each swizzle stick 28 has a width in the range of approximately 400 microns to approximately 800 microns, although other dimensions may be used depending on the application. Similar to the partial cuts 22 a-22 d, the second complete cut 26 b may be made by any appropriate means such as, for example, a rotating or reciprocating saw. The second complete cut 26 b generally should be formed in such a way so as to ensure a depth that is accurate and consistent with the first complete cut 26 a. Similar to the partial cuts 22 a-22 d, the second complete cut 26 b typically has a width in the range of approximately 50 microns to approximately 100 microns. As shown in FIG. 7B, the second complete cut 26 b extends down the full length of the bonded wafer assembly 10.

Referring next to FIGS. 8A and 8B, the process continues by making a third complete cut 26 c in the top wafer 12. The third complete cut 26 c extends entirely through the top wafer 12, but leaves the bottom layer 14 completely intact. By way of example, the third complete cut 26 c is shown in FIG. 8A as being located to the right of the fourth partial cut 22 d, and on the outside of the contact zone 20. Similar to the partial cuts 22 a-22 d, the third complete cut 26 c may be made by any appropriate means such as, for example, a rotating or reciprocating saw. The third complete cut 26 c generally should be formed in such a way so as to ensure a depth that is accurate and consistent with first and second complete cuts 26 a and 26 b. Similar to the partial cuts 22 a-22 d, the third complete cut 26 c typically has a width in the range of approximately 50 microns to approximately 100 microns. As shown in FIG. 8B, the third complete cut 26 c extends down the full length of the bonded wafer assembly 10.

By way of example only, FIGS. 6A-8B illustrate three complete cuts 26 a-26 c being made in the top wafer 12. In practice, any number of complete cuts could be performed depending upon on the number of devices, the number of captured structures to be uncovered, the application, etc. For example, a complete cut may be made between every pair of devices on the bottom wafer, and two partial cuts may be made for each complete cut. In yet another embodiment, the complete cuts 26 may be formed instead as partial cuts similar to the other partial cuts 22 formed in the top wafer 12, thus forming three partial cuts on the top wafer 12 between adjacent rows of die. There would then be three sets of tabs formed between adjacent rows of die, typically with thicknesses in the range of about 30 microns to about 80 microns, although may be other dimensions depending on the specific application. For example, the middle partial cut may be deeper than the others, with the tab being correspondingly thinner, such as about 40 microns or less. Alternatively, there may be a different number of cuts other than three between adjacent die. In some embodiments there may be only two partial cuts as shown in FIG. 5A, or one of those cuts may be a complete cut. Alternatively there may be more than three cuts, such as four or five cuts, in any combination of partial and complete cuts.

Referring now to FIG. 9, there is shown the bonded wafer assembly 10 with the swizzle sticks 28 removed, thereby exposing the contact zones 20. As can be seen in FIG. 9 the portion of the top wafer 12 covering the device 18 a remains intact while the portion of the top wafer 12 previously concealing the contact zones 20 has been removed. Furthermore, FIG. 9 illustrates that the bottom wafer 14 remains unsingulated after removal of the swizzle sticks 28. The removal of the swizzle sticks 28 allows access to the contact zones for processing or testing of the devices 18. By way of example, this processing or testing is illustrated in FIG. 9 with a probe card 30 being used to contact, e.g., bond pads in the contact zones 20.

Referring next to FIG. 10, there is shown a process 1000 for gaining access to captive structures in a bonded wafer assembly without singulation. The process 1000 begins at step 1002, in which a first partial saw cut is made. In steps 1004-1010, all subsequent partial saw cuts are made. Next, a first complete saw cut is made at step 1012 with all subsequent complete saw cuts being made in steps 1014 and 1016. In a typical embodiment, the cuts made in steps 1002-1016 will run in the same direction and will be roughly parallel to each other resulting in, for example, a series of longitudinal or column cuts in the surface of the wafer. In one embodiment, the cuts may be made parallel to columns of contact zones disposed on a bottom wafer. The cutting steps in FIG. 10 may be performed in any order. For example, all partial cuts may be done first, followed by full cuts. Alternatively, the full cuts may be done before the partial cuts. As yet another alternative, all cuts between two rows of adjacent die may be done, followed by cuts between other adjacent die.

Still referring to FIG. 10, at step 1018 the superfluous glass is broken and removed. In step 1018 the glass may be broken by any appropriate method, such as the applicable methods disclosed in U.S. Pat. No. 7,378,293, or those disclosed in co-filed U.S. Patent Application Ser. No. [Attorney Docket No. TI-65482], “Bonded Wafer Assembly System and Method.” For example, pressure may be applied by hand or by any tool designed for such a purpose, either manually or automatically by machine. The removal of the broken glass is accomplished in step 1018, for example by simply turning the wafer over and letting gravity act on the superfluous glass. Alternatively, a vacuum system could also be employed to remove the broken glass. At step 1020, the devices embedded in the wafer are each tested and further processed, e.g., as described above with respect to FIG. 9.

Still referring to FIG. 10, at step 1022, following any desired testing and other processing, the devices are then completely singulated. This is typically accomplished by making complete saw cuts through the bottom wafer between each device pair and parallel to the cuts made in steps 1002-1016, as well as through both the top and the bottom wafers between each device pair in a direction roughly perpendicular to the cuts made in steps 1002-1016. Although this step typically takes place after all the devices are tested and processed, that need not always be the case. The process ends at step 1024.

Overall, the swizzle stick removal process described herein may be performed only in a single direction, removing glass in either the columns or the rows. Alternatively, the process may be performed in both directions, removing glass in a grid pattern. Furthermore, the process may remove glass between all device columns or rows on a wafer, or only between some of the devices on the wafer. For example, if there are bond pads on only one side of a device, and adjacent devices have their bond pads proximate to each other, then only every other column between devices may be removed to provide access to the bond pads.

Although embodiments of the present invention and their advantages have been described in detail herein, it should be understood that various changes, substitutions and alterations can be made herein without departing from the spirit and scope of the invention as defined by the appended claims.

Moreover, the scope of the present application is not intended to be limited to the particular embodiments described in the specification. As one of ordinary skill in the art will readily appreciate from the disclosure of the present invention, processes, machines, manufacture, compositions of matter, means, methods, or steps, presently existing or later to be developed, that perform substantially the same function or achieve substantially the same result as the corresponding embodiments described herein may be utilized according to the present invention. Accordingly, the appended claims are intended to include within their scope such processes, machines, manufacture, compositions of matter, means, methods, or steps. 

What is claimed is:
 1. A method for uncovering captive structures in a bonded wafer assembly, the method comprising: forming a plurality of microelectromechanical (MEMS) devices and rows of contact zones on a bottom wafer; bonding a top wafer to the bottom wafer, thereby covering the MEMS devices and contact zones; cutting a plurality of linear cuts in the top wafer between adjacent MEMS devices and parallel to the rows of contact zones; and removing a segment of the top wafer defined by the plurality of cuts, wherein the bottom wafer remains unsingulated, wherein at least one of the rows of contact zones is uncovered, and wherein the adjacent MEMS devices remain covered.
 2. The method of claim 1, wherein the top wafer comprises a material selected from the group consisting of glass, silicon, and gallium arsenide.
 3. The method of claim 1, wherein the bottom wafer comprises silicon.
 4. The method of claim 1, wherein the cutting the plurality of linear cuts comprises: cutting a first cut partially through the top wafer near one of the adjacent MEMS devices; cutting a second cut partially through the top wafer near another of the adjacent MEMS devices; and cutting a third cut fully through the top wafer between the first and second cuts.
 5. The method of claim 1, wherein the cutting the plurality of linear cuts comprises: cutting a first cut partially through the top wafer near one of the adjacent MEMS devices; cutting a second cut partially through the top wafer near another of the adjacent MEMS devices; and cutting a third cut partially through the top wafer between the first and second cuts.
 6. The method of claim 1, further comprising removing multiple segments of the top wafer.
 7. The method of claim 1, wherein at least one cut of the plurality of cuts extends entirely through the top wafer.
 8. The method of claim 1, wherein at least one cut of the plurality of cuts does not extend through the top wafer, leaving a tab portion of the top wafer under the at least one cut.
 9. The method of claim 8, wherein the tab comprises a thickness of between about 30 microns and about 80 microns.
 10. The method of claim 1, wherein the segment comprises a width of between about 400 microns and about 800 microns, and wherein each cut of the plurality of cuts comprises a width of between about 50 microns and about 100 microns.
 11. The method of claim 1, further comprising, after the removing a segment of the top wafer, cutting through the bottom wafer to singulate the MEMS devices.
 12. A microelectromechanical (MEMS) bonded wafer assembly comprising: an unsingulated bottom wafer; an array of MEMS devices disposed on the bottom wafer, the array having columns and rows; at least one row of bond pads disposed on the bottom wafer for each of the rows of MEMS devices; a top wafer bonded to the bottom wafer in a perimeter around each of the MEMS devices, and between the MEMS devices and their associated bond pads; wherein the top wafer is partially singulated into rows, each top wafer row covering a respective row of the rows of MEMS devices as well as regions between the MEMS devices in the respective row; and wherein the top wafer does not cover the bond pads.
 13. The bonded wafer assembly of claim 11, wherein each top wafer row comprises at least one fractured partial tab.
 14. The bonded wafer assembly of claim 11, wherein the top wafer comprises a material selected from the group consisting of glass, silicon, and gallium arsenide.
 15. The bonded wafer assembly of claim 11, wherein the bottom wafer comprises silicon.
 16. A method of processing a microelectromechanical (MEMS) bonded wafer assembly, wherein the wafer assembly comprises a top wafer bonded to a bottom wafer, and wherein the bottom wafer comprises captive structures, the method comprising: forming a plurality of parallel partial cut pairs extending only partially through the top wafer; removing segments of the top wafer defined by the partial cut pairs, the segments overlying the captive structures disposed therebeneath on the bottom wafer; and processing at least one of the captive structures while the bottom wafer remains unsingulated.
 17. The method of claim 15, further comprising forming a plurality of parallel full cuts extending fully through the top wafer and between respective partial cut pairs.
 18. The method of claim 15, wherein the captive structures are bond pads associated with MEMS devices formed on the bottom wafer.
 19. The method of claim 15, wherein the processing at least one of the captive structures comprises die level testing.
 20. The method of claim 15 wherein the processing at least one of the captive structures comprises accessing the captive structure with a probe card. 